聚丙烯酸树脂Ⅲ动力黏度测定方法的研究
Research of the method on measurement of dynamic viscosity of Polyacrylic Resin Ⅲ
分类号：
出版年·卷·期（页码）：2012,32 (4):0-0
DOI:
10.16155/j.0254-1793.2017.01.01
-----摘要：-------------------------------------------------------------------------------------------
目的: 研究聚丙烯酸树脂Ⅲ的流体特性并建立了该树脂动力黏度测定方法。 方法: 采用马尔文Bohlin Gemini HRnano同轴圆筒式流变仪,在以温度20 ℃,剪切速率10 s-1条件下测定动力黏度。 结果: 结果表明聚丙烯酸树脂Ⅲ为牛顿流体,动力黏度为129.95 MPa·s,30次测定的相对偏差为0.6%。 结论: 方法简便、准确、重复性好,适合用于测定聚丙烯酸树脂Ⅲ的动力黏度。
-----英文摘要：---------------------------------------------------------------------------------------
Objective: To study the Rheology behavior of Polyacrylic ResinⅢand establish a method to measure it's dynamic viscosity. Method: A Malvern Bohlin Gemini HRnano Concentric cylinder rheometer was used to develop the method at the Shear-Rate 10(1/s).Temperature when the test was carried out was 20 ℃. Results: Polyacrylic ResinⅢ was newtonian fluid,whose dynamic viscosity was 129.95 MPa·s(RSD=0.6%,n=30). Conclusion: The Method is convenient,accurate and reproductive for the control of the dynamic viscosity of the Polyacrylic ResinⅢ.
-----参考文献：---------------------------------------------------------------------------------------
[1] Rowe RC,Sheskey PJ,Weller PJ.Translate by Zheng Jun-min(郑俊民译).Handbook of Pharmaceutical Excipients(药用辅料手册).4th(第4版).Beijing(北京):Chemical Industry Press(化学工业出版社),2004.793
[2] Lehmann K.Formulation of controlled release tablets with acrylic risins.Acta Pharm Fenn 1984,93:55
[3] Jovanovic M,Jovicic G,Duvic Z,et al.Effect of fillers and lubricants on acetylsalicylic acid release kinetics from eudragit matrix tablets.Drug Dev Ind Pharm,1997,23(6):595
[4] Umejima H,Kim N-S,Ito T,et al.Preparation and evaluation of Eudragit gels VI:in vivo evaluation of Eudispert rectal hydrogel and Xerogel containing salicylamide.Pharm Sci,1993,82:195
[5] WANG Lin-bo(王林波),JIN Wei(金薇),LE Jian(乐健),et al.Research of method to measure the dynamic viscosity of adapalene gel(阿达帕林凝胶剂动力黏度测定方法的研究).Chin J Pharm Anal(药物分析杂志),2008,28(12):2040
欢迎阅读《药物分析杂志》！您是该文第 1143位读者！